A synthesized benzothiazole containing mono-methacrylate monomer BTTMA was incorporated into Bis-GMA/TEGDMA dental resin system with a series of mass concentration from 5 to 30 wt.% as an antibacterial agent. The influence of BTTMA on physicochemical properties of dental resin system, such as double bond conversion (DC), volumetric shrinkage (VS), flexural strength (FS) and modulus (FM), water sorption (WS) and solubility (SL) were investigated. Direct contact testing and agar diffusion testing were used to evaluate the antibacterial activity of BTTMA containing dental resin. The results showed that BTTMA could endow dental resin with significant antibacterial activity when its concentration reached a certain amount (20 wt.%), and the antibacterial activity of BTTMA containing dental resin was mainly attributed to the immobilized BTTMA instead of the unreacted leachable BTTMA. BTTMA had no negative effect on physicochemical properties of dental resin, and even some BTTMA containing dental resins had advantages like higher DC, lower VS and WS when compared with control resin. Therefore, BTTMA could be considered as a suitable antibacterial agent in dental material, but much more researches concerned about biocompatibility should be done in future to prove whether it could be applied in clinic.
Keywords: Dental resin; antibacterial activity; benzothiazole; physicochemical properties.