Aim and objective: The aim and objective of the study is to evaluate effect of ultraviolet (UV) stabilizer (UV absorber Chimassorb 81) on color change of pigmented silicone elastomer when commercially available (red and yellow), and newly developed pigments (sicotrans red and sicopal brown) were used.
Materials and methods: Two commercially available pigments - red (P112 Brilliant Red) and yellow (P106 Yellow) and two newly developed pigments - sicotrans red and sicopal brown were studied. In total eight groups made up of nine samples each were fabricated using elastomer with the combinations of the above pigments and UV stabilizer (Chimassorb 81). Groups 1, 3, 5, and 7 contain elastomer in combination with sicotrans red, sicopal brown, yellow and red pigments, respectively. Similarly, groups 2, 4, 6, and 8 along with elastomer and pigments (sicotrans sed, sicopal brown, yellow and red, respectively) contain the UV stabilizer (Chimassorb 81). Samples were subjected to aging in an accelerated weathering chamber (Weather-Ometer). Color values CIE (Commission Internationale d'Eclairage) L*, a*, and b * were measured at baseline and after 1000 h of weathering. Change in color (Delta E) was calculated.
Results: All groups showed a significant color change at 1000 h. Groups 1, 2, 3, and 4 showed a statistically significant less change in both colors (sico trans red and sicopal brown) compared to groups 5,6,7, and 8 (commercial pigments-Red and Yellow). Overall, the change in the color in groups with the UV stabilizer (Chimassorb) was less when compared to the groups where the stabilizer was not used.
Conclusion: The newly developed pigment led to increased color stability as compared to commercially available pigments. Addition of UV stabilizer, Chimassorb led to a further reduction in color change of the pigmented elastomer.
Keywords: Color stability; elastomers; ultraviolet stabilizers.