We unprecedentedly report that layered MnO₂ nanosheets were in situ formed onto the surface of covalently bonded graphitic carbon nitride/reduced graphene oxide nanocomposite (g-C₃N₄/rGO), forming sheet-on-sheet structured two dimension (2D) graphitic carbon nitride/reduced graphene oxide/layered MnO₂ ternary nanocomposite (g-C₃N₄/rGO/MnO₂) with outstanding catalytic properties on thermal decomposition of ammonium perchlorate (AP). The covalently bonded g-C₃N₄/rGO was firstly prepared by the calcination of graphene oxide-guanidine hydrochloride precursor (GO-GndCl), following by its dispersion into the KMnO₄ aqueous solution to construct the g-C₃N₄/rGO/MnO₂ ternary nanocomposite. FT-IR, XRD, Raman as well as the XPS results clearly demonstrated the chemical interaction between g-C₃N₄, rGO and MnO₂. TEM and element mapping indicated that layered g-C₃N₄/rGO was covered with thin MnO₂ nanosheets. Furthermore, the obtained g-C₃N₄/rGO/MnO₂ nanocomposite exhibited promising catalytic capacity on thermal decomposition of AP. Upon addition of 2 wt % g-C₃N₄/rGO/MnO₂ ternary nanocomposite as catalyst, the thermal decomposition temperature of AP was largely decreased up by 142.5 °C, which was higher than that of pure g-C₃N₄, g-C₃N₄/rGO and MnO₂, respectively, demonstrating the synergistic catalysis of the as-prepared nanocomposite.
Keywords: covalent coupling; g-C3N4/rGO/MnO2; in situ formation; sheet-on-sheet; synergistic effect.