So far, there is no report regarding the micro-Raman vibrational fingerprint of the bonds between 10-methacryloyloxy-decyl dihydrogen phosphate (10-MDP) and zirconia ceramics. Thus, the aim of this study was to identify the Raman vibrational peaks related to the bonds of 10-MDP with zirconia, as well as the influence on microshear bond strength. Micro-Raman spectroscopy was employed to assess the vibrational peak of 10-MDP binding to zirconia. Microshear bond strength of the dual-cure resin cement to zirconia with the presence of 10-MDP in composition of experimental ceramic primer and self-adhesive resin cement was also surveyed. Statistical analysis was performed by one-way ANOVA and Tukey's test (p < 0.05). Peaks at 1545 cm-1 and 1562 cm-1 were found to refer to zirconia binding with 10-MDP. The presence of 10-MDP in both experimental ceramic primer and self-adhesive resin cement improved microshear bond strength to zirconia ceramic. It can be concluded that the nondestructive method of micro-Raman spectroscopy was able to characterize chemical bonds of 10-MDP with zirconia, which improves the bond strengths of resin cement.