Lead halide perovskite solar cells with remarkable power conversion efficiency have attracted much attention in recent years. However, there still exist many problems with their use that are not completely understood, and further studies are needed. Herein, the hole-transport layer dependence of the photovoltaic performance of perovskite solar cells is investigated in detail. It is found that devices freshly prepared using pristine 2,2',7,7'-tetrakis-(N,N-di-p-methoxyphenylamine)-9,9'-spirobifluorene (spiro-OMeTAD) and Li-doped spiro-OMeTAD as hole-transport layers exhibit S-shaped current density-voltage curves with poor fill factors. The devices show progressively improved fill factors and efficiencies upon exposure to air, which is attributed to air-induced conductivity improvement in the spiro-OMeTAD layer. After introducing a cobalt salt dopant (FK209) into the spiro-OMeTAD layer, the corresponding devices show remarkable performance without the need of air exposure. These results confirm that the dopant not only increases the conductivity of spiro-OMeTAD layer, but also tunes the surface potential, which helps to improve charge transport and reduce the recombination loss.
Keywords: conductivity; photovoltaic performance; solar cells; spirobifluorenes; surface potential.
© 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.