Novel biodegradable films were prepared by blending guar gum, chitosan and poly (vinyl alcohol) having mint (ME) and grapefruit peel (GE) extracts and crosslinked with nontoxic tetraethoxysilane (TEOS). The co-concentration effect of TEOS with natural extracts on the films was studied. FTIR analysis confirmed the presence of incorporated components and the developed interactions among the polymer chains. The surface morphology of the films by SEM showed the hydrophilic character due to porous network structure. The films having both ME and GE with maximum amount of crosslinker (100μL), showed maximum swelling (58g/g) and stability while the optical properties showed increased protection against UV light. This film sample showed compact network structure which enhanced the ultimate tensile strength (40.03MPa) and elongation at break (104.8%). ME/GE conferred the antioxidant properties determined by radical scavenging activity and total phenolic contents (TPC) as ME films have greater TPC compared to GE films. The soil burial test exhibited the degradation of films rapidly (6days) confirming their strong microbial activity in soil. The lower water vapour transmission rate and water vapour permeability showed better shelf life; hence, these biodegradable films are environmental friendly and have potential for food and other packaging.
Keywords: Chitosan; Food packaging; Guar gum; PVA; Silane crosslinker.
Copyright © 2017 Elsevier B.V. All rights reserved.