Adequate selection of material constituents and test methods are necessary for workability specifications and performance of hardened concrete. An experimental program was performed to evaluate the suitability of various test methods for workability assessment and to propose performance specifications of prestressed concrete. In total, 33 self-consolidating concrete (SCC) mixtures made with various mixture proportioning parameters, including maximum size and type of aggregate, type and content of binder, and w/cm were evaluated. Correlations among various test results used in evaluating the workability responses are established. It is recommended that SCC should have slump flow values of 635-760 mm. To ensure proper filling capacity greater than 80%, such concrete should have a passing ability that corresponds to L-box blocking ratio (h₂/h₁) ≥ 0.5, J-Ring flow of 570-685 mm, slump flow minus J-Ring flow diameter ≤75 mm. Moreover, Stable SCC should develop a column segregation index lower than 5%, and rate of settlement at 30 min of 0.27%/h for SCC proportioned with 12.5 or 9.5 mm MSA. It is recommended that SCC should have a plastic viscosity of 100-225 Pa·s and 100-400 Pa·s for concrete made with crushed aggregate and gravel, respectively, to ensure proper workability.
Keywords: mixture proportioning; prestressed concrete; rheology; self-consolidating concrete; test method; workability.