The literature shows that inorganic phase change materials (PCM) have been very seldom microencapsulated, so this study aims to contribute to filling this research gap. Bischofite, a by-product from the non-metallic industry identified as having good potential to be used as inorganic PCM, was microencapsulated by means of a fluidized bed method with acrylic as polymer and chloroform as solvent, after compatibility studies of both several solvents and several polymers. The formation of bischofite and pure MgCl₂·6H₂O microcapsules was investigated and analyzed. Results showed an efficiency in microencapsulation of 95% could be achieved when using 2 min of fluidization time and 2 kg/h of atomization flow. The final microcapsules had excellent melting temperatures and enthalpy compared to the original PCM, 104.6 °C and 95 J/g for bischofite, and 95.3 and 118.3 for MgCl₂·6H₂O.
Keywords: MgCl2·6H2O; bischofite; fluidization; inorganic; microencapsulation; phase change material.