Purpose: Currently, the foreign surfaces of various extracorporeal circulation devices are coated with a biocompatible polymer coating agent (BPA), which creates a hydrophilic blood-contacting layer to reduce thrombogenicity, while the membranes in hemodialyzers are not. We aimed to clarify other side effects of BPA-coated membranes by examining the diffusion performance in in vitro experiments.
Methods: We used a polyethersulfone membrane (sieving coefficient of albumin is ≤0.01) coated with BPA product, SEC-1TM (Toyobo), in a hemodialyzer. To estimate the diffusion rates of a wide range of molecules, 2 L of saline containing vancomycin, lysozyme, and albumin were recirculated in the circuit configured with a hemodialyzer, and dialyzed continuously using water. The concentrations of sodium, vancomycin, lysozyme, and albumin were measured every 5 minutes for 30 minutes and compared in experiments with BPA-coated (n = 4) and BPA-noncoated (n = 4) membranes.
Results: The removal rates of sodium and vancomycin after 5 minutes of dialysis (n = 24) were significantly higher in BPA-coated than noncoated membranes, while those of lysozyme and albumin were not significantly different. The removal rates of sodium and vancomycin after 30 minutes of dialysis (n = 4) were significantly higher, and those of lysozyme were significantly lower in BPA-coated than noncoated membranes, while those of albumin were not significantly different.
Conclusions: The preliminary study suggests that BPA-coated membranes enhanced the diffusion rate of molecules with low and middle molecular weight without affecting the sieving coefficient of albumin. Thus, BPA coating can enhance the dialysis performance of membranes.