Wire arc additive manufacturing (WAAM) technique is a cost-competitive and efficient technology to produce large structure components in industry domains. Mechanical properties are mainly dominated by the microstructure of the components, which is deeply affected by the molten pool size. In this work, to investigate the effect of the molten pool size on microstructure and mechanical properties of the components, a series of Ti-6Al-4V alloy blocks with different width of molten pool (WMP) ranging from 7 mm to 22 mm were deposited by adjusting the wire feed speed (WFS) from 100 cm/min to 500 cm/min. It is interesting to find that the macrostructure changes from columnar grains to equiaxial grains, and then returns to large columnar grains with the increase of WMP, which is mainly caused by the different cooling rates and thermal gradients. Nonetheless, the tensile properties of the components have a tendency to decline with the increase of WMP.
Keywords: Ti-6AL-4V; microstructure; molten pool size; tensile properties; wire arc additive manufacturing.