This work describes the synthesis and characterization of pillared clays using a new pillaring method: the reuse of the pillaring solution. First, an Al pillared clay (PILC) was synthesized, and after filtration, the pillaring agent was stored and reused for an additional three pillaring procedures (P1, P2, and P3). The filtered pillaring solution was stored for one year and then reused for one additional pillaring procedure (P4). The samples were analyzed using XRD, N₂ physisorption measurements and chemical analysis (EDX). All of the samples exhibited basal spacings larger than 17 Å and BET surface areas greater than 160 m²/g. After the P4 pillaring, the pillaring agent was precipitated with a Na₂SO₄ solution, and the resulting solid was analyzed using XRD and SEM. The results indicated that even after a total of five pillaring procedures, Al13 ions were still present in solution. Therefore, it is possible to reuse the pillaring solution four times and to even store the solution for one year, which is important from an industrial perspective.
Keywords: Keggin ion; pillaring solution; reutilization.