Bio-composites based on polyhydroxyalkanoates (PHAs) and fibres of Posidonia oceanica (PO) were investigated to assess their processability by extrusion, mechanical properties, and potential biodegradability in a natural marine environment. PHAs were successfully compounded with PO fibres up to 20 wt % while, at 30 wt % of fibres, the addition of 10 wt % of polyethylene glycol (PEG 400) was necessary to improve their processability. Thermal, rheological, mechanical, and morphological characterizations of the developed composites were conducted and the degradation of composite films in a natural marine habitat was evaluated in a mesocosm by weight loss measure during an incubation period of six months. The addition of PO fibres led to an increase in stiffness of the composites with tensile modulus values about 80% higher for composites with 30 wt % fibre (2.3 GPa) compared to unfilled material (1.24 GPa). Furthermore, the impact energy markedly increased with the addition of the PO fibres, from 1.63 (unfilled material) to 3.8 kJ/m² for the composites with 30 wt % PO. The rate of degradation was markedly influenced by seawater temperature and significantly promoted by the presence of PO fibres leading to the total degradation of the film with 30 wt % PO in less than six months. The obtained results showed that the developed composites can be suitable to manufacture items usable in marine environments, for example, in natural engineering interventions, and represent an interesting valorisation of the PO fibrous wastes accumulated in large amounts on coastal beaches.
Keywords: Posidonia oceanica; composites; marine degradation; polyhydroxyalkanoates.