In this study, a novel membrane for the separator in a lithium-ion (Li-ion) battery was proposed via a mechanically pressed process with a poly(vinylidene fluoride) (PVDF) nanofiber subject and polyethylene terephthalate (PET) microfiber support. Important physical properties, such as surface morphology, wettability, and heat stability were considered for the PET-reinforced PVDF nanofiber (PRPN) hybrid separator. Images of scanning electron microscopy (SEM) showed that the PRPN hybrid separator had a homogeneous pore size and high porosity. It can wet out in battery electrolytes completely and quickly, satisfying wettability requirements. Moreover, the electrolyte uptake was higher than that of dry-laid and wet-laid nonwovens. For heat stability, no shrink occurred even when the heating temperature reached 135 °C, demonstrating thermal and dimensional stability. Moreover, differential scanning calorimetry (DSC) showed that the PRPN hybrid separator possessed a shutdown temperature of 131 °C, which is the same as conventional separators. Also, the meltdown temperature reached 252 °C, which is higher than the shutdown temperature, and thus can protect against internal cell shorts. The proposed PRPN hybrid separator is a strong candidate material for utilization in Li-ion batteries.
Keywords: Li-ion battery; PVDF nanofiber membrane; hybrid separator; thermal stability; wettability.