Hexavalent chromium adsorption from aqueous solution using carbon nano-onions (CNOs)

Abstract

The capacity of carbon nano-onions (CNOs) to remove hexavalent chromium (Cr(VI)) from aqueous solution was investigated. Batch experiments were performed to quantify the effects of the dosage rate, pH, counter ions, and temperature. The adsorption of Cr(VI) onto CNOs was best described by a pseudo-second order rate expression. The adsorption efficiency increased with increasing adsorbent dosage and contact time and reached equilibrium in 24 h. The equilibrium data showed better compliance with a Langmuir isotherm than a Freundlich isotherm. Effective removal of Cr(VI) was demonstrated at pH values ranging from 2 to 10. The adsorption capacity of Cr(VI) was found to be highest (82%) at pH 3.4 and greatly depended on the solution pH. We found that Cr(VI) adsorption decreased with increasing pH over the pH range of 3.4-10. The adsorption capacity increased dramatically when the temperature increased from 10 °C to 50 °C regardless of the amount of CNOs used. Cr(VI) removal decreased by ∼13% when Zn(II), Cu(II), and Pb(II) were present, while there were no significant changes observed when NO₃^- or SO₄^2- was present. The overall results support that CNOs can be used as an alternative adsorbent material to remove Cr(VI) in the water treatment industry.

Keywords: Adsorption capacity; Adsorption isotherm; Adsorption kinetics; Carbon nano-onions; Hexavalent chromium; Metal adsorption.