Cu supported on mesoporous ceria: water gas shift activity at low Cu loadings through metal-support interactions

Dimitriy Vovchok; Curtis J Guild; Jordi Llorca; Wenqian Xu; Tahereh Jafari; Panteha Toloueinia; David Kriz; Iradwikanari Waluyo; Robert M Palomino; José A Rodriguez; Steven L Suib; Sanjaya D Senanayake

doi:10.1039/c7cp02378b

Cu supported on mesoporous ceria: water gas shift activity at low Cu loadings through metal-support interactions

Phys Chem Chem Phys. 2017 Jul 21;19(27):17708-17717. doi: 10.1039/c7cp02378b. Epub 2017 Jun 27.

Authors

Affiliations

¹ Department of Chemistry, Stony Brook University, Stony Brook, NY 11794, USA and Chemistry Department, Brookhaven National Laboratory, Upton, NY 11973, USA. ssenanay@bnl.gov.
² Department of Chemistry, University of Connecticut, Storrs, CT 06269, USA. Steven.suib@uconn.edu.
³ Institute of Energy Technologies, Department of Chemical Engineering and Barcelona Research Center in Multiscale Science and Engineering, Technical University of Catalonia, 08019 Barcelona, Spain.
⁴ Advanced Photon Source, Argonne National Laboratory, Argonne, IL 60439, USA.
⁵ Institute of Material Sciences, University of Connecticut, Storrs, CT 06269, USA.
⁶ National Synchrotron Light Source II, Brookhaven National Laboratory, Upton, NY 11973, USA.
⁷ Chemistry Department, Brookhaven National Laboratory, Upton, NY 11973, USA. ssenanay@bnl.gov.
⁸ Department of Chemistry, University of Connecticut, Storrs, CT 06269, USA. Steven.suib@uconn.edu and Institute of Material Sciences, University of Connecticut, Storrs, CT 06269, USA.

PMID: 28653713
DOI: 10.1039/c7cp02378b

Abstract

We have synthesized and tested a highly active Cu doped mesoporous CeO₂ catalyst system for the low temperature water-gas shift (WGS) reaction. While typical oxide-supported copper WGS catalysts are characterized by high copper loadings (30-40%), the morphological properties of the mesoporous CeO₂ material enable high catalytic activity at copper loadings as low as 1%. Operando X-ray diffraction, in situ X-ray absorption near-edge structure spectroscopy (XANES), and operando diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) methods were used to probe the interactions between the metal and mesoporous oxide components under reaction conditions. Copper was observed to undergo reduction from oxide to metal under WGS conditions at 150 °C, while the CeO₂ lattice was observed to expand upon heating, indicating Ce³⁺ formation correlated with CO₂ production. The active state of the catalysts was confirmed by in situ XANES to contain Cu⁰ and partially reduced CeO₂. DRIFTS analysis revealed carboxyl species bound to copper during reduction, as well as formate and carbonate surface species on ceria. Lower concentrations of copper were observed to foster enhanced metal-support interactions.