The purpose of this work was to investigate the effect of strontium partial replacement for calcium on the crystallization behavior, microstructure and solubility of fluorapatite glass-ceramics. Four glass compositions were prepared with increasing amounts of strontium partially replacing calcium. The crystallization behavior was analyzed by differential scanning calorimetry and X-ray diffraction (XRD). The microstructure was investigated by scanning electron microscopy. The chemical solubility was quantified according to ISO standard 10993-14. The amount of strontium released in solution after incubation in TRIS-HCl or citric acid buffer was measured by atomic absorption spectroscopy. XRD analyses revealed that partially substituted strontium-fluorapatite and strontium-åkermanite crystallized after strontium additions. The lattice cell volume of both phases increased linearly with the amount of strontium in the composition. Strontium additions led to a reduction in crystal size and an increase in crystal number density. The chemical solubility and amount of strontium released in solution increased linearly with the amount of strontium present in the composition in both TRIS-HCl and citric acid buffers. Total amounts of strontium released reached a maximum of 547 ± 80 ppm in TRIS-HCl and 1252 ± 290 ppm in citric acid buffer for the glass composition with the highest amount of strontium. For all strontium-containing compositions, the amount released in TRIS-HCl continued to increase between 70 and 120 h, indicating sustained release rather than burst release. © 2017 Wiley Periodicals, Inc. J Biomater Res Part B: 106B: 1421-1430, 2018.
Keywords: fluorapatite; glass-ceramic; solubility; strontium; åkermanite.
© 2017 Wiley Periodicals, Inc.