Supercapacitors have been one of the highest potential candidates for energy storage because of their significant advantages beyond rechargeable batteries in terms of large power density, short recharging time, and long cycle lifespan. In this work, Cu-Co sulfides with uniform flower-like structure have been successfully obtained via a traditional two-step hydrothermal method. The as-fabricated Cu-Co sulfide vulcanized from precursor (P-Cu-Co sulfide) is able to deliver superior specific capacitance of 592 F g-1 at 1 A g-1 and 518 F g-1 at 10 A g-1 which are surprisingly about 1.44 times and 2.39 times higher than those of Cu-Co oxide electrode, respectively. At the same time, excellent cycling stability of P-Cu-Co sulfide is indicated by 90.4% capacitance retention at high current density of 10 A g-1 after 3000 cycles. Because of the introduction of sulfur during the vulcanization process, these new developed sulfides can get more flexible structure and larger reaction surface area, and will own richer redox reaction sites between the interfaces of active material/electrolyte. The uniform flower-like P-Cu-Co sulfide electrode materials will have more potential alternatives for oxides electrode materials in the future.
Keywords: binder-free; copper-cobalt sulfide; electrode material; hydrothermal method.