Sol-gel-derived bioactive glass nanoparticle-incorporated glass ionomer cement with or without chitosan for enhanced mechanical and biomineralization properties

Abstract

Objective: This study investigated the mechanical and in vitro biological properties (in immortalized human dental pulp stem cells (ihDPSCs)) of bioactive glass nanoparticle (BGN)-incorporated glass ionomer cement (GIC) with or without chitosan as a binder.

Methods: After the BGNs were synthesized and characterized, three experimental GICs and a control (conventional GIC) that differed in the additive incorporated into a commercial GIC liquid (Hy-bond, Shofu, Japan) were produced: BG5 (5wt% of BGNs), CL0.5 (0.5wt% of chitosan), and BG5+CL0.5 (5wt% of BGNs and 0.5wt% of chitosan). After the net setting time was determined, weight change and bioactivity were analyzed in simulated body fluid (SBF) at 37°C. Mechanical properties (compressive strength, diametral tensile strength, flexural strength and modulus) were measured according to the incubation time (up to 28 days) in SBF. Cytotoxicity (1day) and biomineralization (14 days), assessed by alizarin red staining, were investigated using an extract from GIC and ihDPSCs. Data were analyzed using one-way analysis of variance (ANOVA) followed by Tukey's post hoc test; p<0.05.

Results: BGNs were sol-gel synthesized to be approximately 42nm in diameter with a spherical morphology and amorphous structure. After the bioactivity and suspension ability of the BGNs were confirmed, all the experimental GIC groups had setting times of less than 6min and approximately 1% weight loss after 28days of incubation. In addition, BGNs incorporated into GIC (BG5 and BG5+CL0.5) exhibited surface bioactivity. The mechanical properties were increased in the BGN-incorporated GICs compared to those in the control (p<0.05). Without cytotoxicity, the biomineralization capacity was ranked in the order BG5, BG5+CL0.5, control, and CL0.5 (p<0.05).

Significance: BGN-incorporated GIC showed enhanced mechanical properties such as compressive, diametral tensile and flexural strength as well as in vitro biomineralization properties in ihDPSCs without cytotoxicity. Therefore, the developed BGN-incorporated GIC is a promising restorative dental material, although further in vivo investigation is needed before clinical application.

Keywords: Bioactive glass nanoparticle; Biomineralization; Chitosan; Glass ionomer cement; Human dental pulp stem cells; Mechanical properties.