From polyethylene waxes to HDPE using an α,α'-bis(arylimino)-2,3:5,6-bis(pentamethylene)pyridyl-chromium(iii) chloride pre-catalyst in ethylene polymerisation

Abstract

Five examples of α,α'-bis(arylimino)-2,3:5,6-bis(pentamethylene)pyridyl-chromium(iii) chlorides (aryl = 2,6-Me₂Ph Cr1, 2,6-Et₂Ph Cr2, 2,6-i-Pr₂Ph Cr3, 2,4,6-Me₃Ph Cr4, 2,6-Et₂-4-MePh Cr5) have been synthesized by the one-pot template reaction of α,α'-dioxo-2,3:5,6-bis(pentamethylene)pyridine, CrCl₃·6H₂O and the corresponding aniline. The molecular structures of Cr1 and Cr4 reveal distorted octahedral geometries with the N,N,N-ligand adopting a mer-configuration. On activation with an aluminium alkyl co-catalyst, Cr1-Cr5 exhibited high catalytic activities in ethylene polymerization and showed outstanding thermal stability operating effectively at 80 °C with activities up to 1.49 × 10⁷ g of PE (mol of Cr)^-1 h^-1. Significantly, the nature of the co-catalyst employed had a dramatic effect on the molecular weight of the polymeric material obtained. For example, using diethylaluminium chloride (Et₂AlCl) in combination with Cr4 gave high density/high molecular weight polyethylene with broad molecular weight distributions (30.9-39.3). By contrast, using modified methylaluminoxane (MMAO), strictly linear polyethylene waxes of lower molecular weight and narrow molecular weight distribution (1.6-2.0) were obtained with vinyl end-groups.