Bone tissue engineering scaffolds for the reconstruction of large bone defects should simultaneously promote osteogenic differentiation and avoid postoperative infection. Herein, we develop, for the first time, Ag-loaded MgSrFe-layered double hydroxide/chitosan (Ag-MgSrFe/CS) composite scaffold. This scaffold exhibits three-dimensional interconnected macroporous structure with a pore size of 100-300 μm. The layered double hydroxide nanoplates in the Ag-MgSrFe/CS show lateral sizes of 200-400 nm and thicknesses of ∼50 nm, and the Ag nanoparticles with particle sizes of ∼20 nm are uniformly dispersed on the scaffold surfaces. Human bone marrow-derived mesenchymal stem cells (hBMSCs) present good adhesion, spreading, and proliferation on the Ag-MgSrFe/CS composite scaffold, suggesting that the Ag and Sr elements in the composite scaffold have no toxicity to hBMSCs. When compared with MgFe/CS composite scaffold, the Ag-MgSrFe/CS composite scaffold has better osteogenic property. The released Sr2+ ions from the composite scaffold enhance the alkaline phosphatase activity of hBMSCs, promote the extracellular matrix mineralization, and increase the expression levels of osteogenic-related RUNX2 and BMP-2. Moreover, the Ag-MgSrFe/CS composite scaffold possesses good antibacterial property because the Ag nanoparticles in the composite scaffold effectively prevent biofilm formation against S. aureus. Hence, the Ag-MgSrFe/CS composite scaffold with excellent osteoinductivity and antibacterial property has a great potential for bone tissue engineering. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 863-873, 2018.
Keywords: Ag nanoparticles; antibacterial property; chitosan; layered double hydroxide; osteogenic property.
© 2017 Wiley Periodicals, Inc.