We report on the synthesis of the zirconia-manganese carbonate ZrOx(x %)-MnCO3 catalyst (where x=1-7) that, upon calcination at 500 °C, is converted to zirconia-manganese oxide ZrOx(x %)-Mn2O3 . We also present a comparative study of the catalytic performance of the both catalysts for the oxidation of benzylic alcohol to corresponding aldehydes by using molecular oxygen as the oxidizing agent. ZrOx(x %)-MnCO3 was prepared through co-precipitation by varying the amounts of Zr(NO3)4 (w/w %) in Mn(NO3)2. The morphology, composition, and crystallinity of the as-synthesized product and the catalysts prepared upon calcination were studied by using scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray spectroscopy, and powder X-ray diffraction. The surface areas of the catalysts [133.58 m2 g-1 for ZrOx(1 %)-MnCO3 and 17.48 m2 g-1 for ZrOx(1 %)-Mn2O3 ] were determined by using the Brunauer-Emmett-Teller method, and the thermal stability was assessed by using thermal gravimetric analysis. The catalyst with composition ZrOx(1 %)-MnCO3 pre-calcined at 300 °C exhibited excellent specific activity (48.00 mmolg-1 h-1) with complete conversion within approximately 5 min and catalyst cyclability up to six times without any significant loss in activity. The specific activity, turnover number and turnover frequency achieved is the highest so far (to the best of our knowledge) compared to the previously reported catalysts used for the oxidation of benzyl alcohol. The catalyst showed selectivity for aromatic alcohols over aliphatic alcohols.
Keywords: benzyl alcohol oxidation; manganese carbonate; manganese oxide; mixed metal oxides; zirconia.