A new family of Ni-, Co-, and Cr-doped Zn-containing magnetic oxide nanoparticles (NPs) stabilized by polyphenylquinoxaline (PPQ) and hyperbranched pyridylphenylene polymer (PPP) has been developed. These NPs have been synthesized by thermal decomposition of Zn and doping metal acetylacetonates in the reaction solution of preformed magnetite NPs, resulting in single-crystal NPs with spinel structure. For the PPQ-capped NPs, it was demonstrated that all three types of metal species (Fe, Zn, and a doping metal) reside within the same NPs, the surface of which is enriched with Zn and a doping metal, while the deeper layers are enriched with Fe. The Cr-doped NPs at the high Cr loading are an exception due to favored deposition of Cr on magnetite located in the NP depth. The PPP-capped NPs exhibit similar morphology and crystallinity; however, the detailed study of the NP composition was barred due to the high PPP amount retained on the NP surface. The catalyst testing in syngas conversion to methanol demonstrated outstanding catalytic properties of doped Zn-containing magnetic oxides, whose activities are dependent on the doping metal content and on the stabilizing polymer. The PPP stabilization allows for better access to the catalytic species due to the open and rigid polymer architecture and most likely optimized distribution of doping species. Repeat experiments carried out after magnetic separation of catalysts from the reaction mixture showed excellent catalyst stability even after five consecutive catalytic runs.
Keywords: doping; hyperbranched; magnetic; methanol synthesis; nanoparticle; polymer; zinc.