The biomimetic remineralization of apatite-depleted dentin is a potential method for enhancing the durability of resin-dentin bonding. To advance this strategy from its initial proof-of-concept design, we sought to investigate the characteristics of polyacrylic acid (PAA) adsorption to desorption from type I collagen and to test the mineralization ability of PAA-bound collagen. Portland cement and β-tricalcium phosphate (β-TCP) were homogenized with a hydrophilic resin blend to produce experimental resins. The collagen fibrils reconstituted on nickel (Ni) grids were mineralized using different methods: (i) group I consisted of collagen treated with Portland cement-based resin in simulated body fluid (SBF); (ii) group II consisted of PAA-bound collagen treated with Portland cement-based resin in SBF; and (iii) group III consisted of PAA-bound collagen treated with β-TCP-doped Portland cement-based resin in deionized water. Intrafibrillar mineralization was evaluated using transmission electron microscopy. We found that a carbonyl-associated peak at pH 3.0 increased as adsorption time increased, whereas a hydrogen bond-associated peak increased as desorption time increased. The experimental resins maintained an alkaline pH and the continuous release of calcium ions. Apatite was detected within PAA-bound collagen in groups II and III. Our results suggest that PAA-bound type I collagen fibrils can be mineralized using Portland cement-based resins.
Keywords: biomimetics; dentin; type I collagen.
© 2016 Eur J Oral Sci.