The objectives of this study were to fabricate porous scaffolds using decellularized meniscus, and to explore a preferable crosslinking condition to enhance mechanical properties of scaffolds. Moreover, the microstructure, porosity, biodegradation and cytotoxicity were also evaluated. EDAC or GTA in different concentration was used to crosslink scaffolds. FTIR demonstrated functional groups change in crosslinking process. SEM photography showed that crosslinked scaffolds had blurry edges, which resulted scaffolds crosslinked by 1.2mol/l EDAC had smaller porosity than other groups. The structure change enhanced antidegradation property. After immersing in enzyme solution for 96h, scaffolds crosslinked by GTA and EDAC could maintain their mass >70% and 80%. Most importantly, mechanical properties of crosslinked scaffolds were also improved. Uncrosslinked Scaffolds had only 0.49kPa in compression modulus and 12.81kPa in tensile modulus. The compression and tensile modulus of scaffolds crosslinked by 1.0% GTA were 1.42 and 567.44kPa respectively. The same value of scaffolds crosslinked by 1.2mol/l EDAC were 1.49 and 532.50kPa. Scaffolds crosslinked by 1.0% and 2.5% GTA were toxic to cells, while EDAC groups showed no cytotoxicity. Chondrocytes could proliferate and infiltrate within scaffolds after seeding. Overall, 1.2mol/l EDAC was a preferable crosslinking condition.
Keywords: Carbodiimides; Crosslinking; Degradation; Glutaraldehyde; Mechanical properties; Meniscus scaffolds.
Copyright © 2016 Elsevier B.V. All rights reserved.