Ultrathin noble metal nanosheets with atomic thickness exhibit abnormal electronic, surfacial, and photonic properties due to the unique two-dimensional (2D) confinement effect, which have attracted intensive research attention in catalysis/electrocatalysis. In this work, the well-defined ultrathin Rh nanosheet nanoassemblies with dendritic morphology are synthesized by a facile hydrothermal method with assistance of poly(allylamine hydrochloride) (PAH), where PAH effectively acts as the complexant and shape-directing agent. Transmission electron microscopy and atomic force microscopy images reveal the thickness of 2D Rh nanosheet with (111) planes is only ca. 0.8-1.1 nm. Nitrogen adsorption-desorption measurement displays the specific surface area of the as-prepared ultrathin Rh nanosheet nanoassemblies is 139.4 m2 g-1, which is much bigger than that of homemade Rh black (19.8 m2 g-1). Detailed catalytic investigations display the as-prepared ultrathin Rh nanosheet nanoassemblies have nearly 20.4-fold enhancement in mass-activity for the hydrolysis of ammonia borane as compared with homemade Rh black.
Keywords: Rh nanoassemblies; ammonia borane; catalytic activity; hydrogen generation; nanosheets.