A new protocol to synthesize size-controlled Au nanoparticles (NPs) loaded onto vertically aligned anatase TiO2 nanotubes arrays (TNTAs) prepared by electrochemical anodization is reported. Ligand-free Au NPs (<10 nm) were deposited onto anatase TNTAs supports, finely tuning the Au loading by controlling the immersion time of the support into metal vapor synthesis (MVS)-derived Au-acetone solutions. The Au/TNTAs composites were characterized by electron microscopies (SEM, (S)TEM), X-ray diffraction, X-ray photoelectron spectroscopy, and UV-vis spectroscopy. Their photocatalytic efficiency was evaluated in toluene degradation in air under ambient conditions without thermal or chemical postsynthetic treatments. The role of Au loadings was pointed out, obtaining a three times enhancement of the pristine anatase TNTAs activity with the best sample containing 3.3 μg Au cm-2.
Keywords: Au nanoparticles; anatase; electrochemical anodization; metal vapor synthesis; nanotubes arrays; photocatalysis; titanium dioxide.