The single-bath electrochemical deposition of CuInSe2 often leads to short-circuit behavior of the resulting solar cells due to the high shunt conductance. In this study, in an attempt to resolve this problem, the influence of the Se precursor concentration (CSe) on electrodeposited CuInSe2 films and solar cell devices is examined in the CSe range of 4.8 to 12.0 mM in selenite-based aqueous solutions containing Cu and In chlorides along with sulfamic acid (H3NSO3) and potassium hydrogen phthalate (C8H5KO4) additives. As CSe increases, the CuInSe2 layers become porous, and the grain growth of the CuInSe2 phase is restricted, while the parasitic shunting problem was markedly alleviated, as unambiguously demonstrated by measurements of the local current distribution. Due to these ambivalent influences, an optimal value of CSe that achieves the best quality of the films for high-efficiency solar cells is identified. Thus, the device prepared with 5.2 mM Se exhibits a power-conversion efficiency exceeding 10% with greatly improved device parameters, such as the shunt conductance and the reverse saturation current. The rationale of the present approach along with the physicochemical origin of its conspicuous impact on the resulting devices is discussed in conjunction with the electro-crystallization mechanism of the CuInSe2 compound.
Keywords: CuInSe2; conductive phases; electrodeposition; single-bath; thin-film solar cells.