Magnetic solid-phase extraction using nanoporous three dimensional graphene hybrid materials for high-capacity enrichment and simultaneous detection of nine bisphenol analogs from water sample

Abstract

The synthesis of a magnetic nanoporous three dimensional graphene (3DG)/ZnFe2O4 composite has been achieved. Through formation of graphene hydrogel, ZnFe2O4 magnetic particles was successfully introduced into the nanoporous 3DG, resulting in a magnetic porous carbon material. The morphology, structure, and magnetic behavior of the as-prepared 3DG/ZnFe2O4 were characterized by using the techniques of SEM, XRD, BET, VSM, FTIR, Raman and TGA. The 3DG/ZnFe2O4 has a high specific surface area and super paramagnetism. Its performance was evaluated by the magnetic solid-phase extraction of nine bisphenol analogs (BPs) from water samples followed by HPLC analysis, and showed excellent adsorption capability for the nine target compounds. Under optimized condition, the lower method detection limits (0.05-0.18ngmL(-1)), the higher enrichment factors (800 fold) and good recoveries (95.1-103.8%) with relative standard deviation (RSD) values less than 6.2% were achieved. The results indicated that the developed method based on the use of 3DG/ZnFe2O4 as the magnetic adsorbent has the advantages of convenience and high efficiency, and can be successfully applied to detect the nine BPs in real water samples.

Keywords: Bisphenol analogs; Magnetic solid-phase extraction; Three dimensional graphene/ZnFe(2)O(4); Water sample.