A series of samples with varying growth pressure are grown and their optical and structural properties are investigated. It is found that the residual carbon concentration decreases when the reactor pressure increases from 80 to 450 Torr during the InGaN/GaN multiple quantum well growth. It results in an enhanced peak intensity of electroluminescence because carbon impurities can induce deep energy levels and act as non-radiative recombination centers in InGaN layers.