Purpose: To investigate the bond strength performance of multimode adhesives (MMAs) to indirect resin composite and lithium disilicate glass ceramic after 24 hours or one year of water storage.
Methods and materials: Thirty flat and polished plates of indirect resin composite (Epricord) and thirty lithium disilicate glass ceramic plates (IPS e.max Press) were prepared. Surfaces were pretreated using sandblasting (indirect resin composite) or hydrofluoric acid (glass-based ceramic). Specimens were bonded with one of two MMAs (Scotchbond Universal [SBU] or All-Bond Universal [ABU]) or ceramic primer and hydrophobic bonding (RelyX Ceramic Primer and Adper Scotchbond Multi-Purpose Bond) as a control (n=10). Resin cement cylinders (0.75 mm in diameter × 0.5 mm in height) were bonded to both substrate surfaces using the respective adhesives. After 24 hours or one year of water storage, bonding performance was measured by microshear bond strength (MSBS) testing. Results were analyzed using three-way ANOVA with Bonferroni post hoc tests (α=0.05).
Results: For indirect resin composite, significantly higher MSBS values were found for ABU after 24 hours (ABU > SBU = control); however, no significant difference among the adhesives was observed after one year (p>0.05). For glass-based ceramic, significantly different bond strengths were observed among the adhesives after 24 hours (control = ABU > SBU) and one year (control > SBU = ABU; p<0.05).
Conclusions: Both MMAs tested can be considered effective alternatives for bonding to sandblasted indirect resin composite after aging, as they showed similar bond performance to that of the control group. However, separate bottles of silane bonding resin showed higher MSBS values and more durable bonding for etched glass-based ceramic.