Porous metal oxide architectures coated with a thin layer of carbon are attractive materials for energy storage applications. Here, a series of porous metal oxide (e.g., vanadium oxides, molybdenum oxides, manganese oxides) foams with/without nitrogen-doped carbon (N-C) coating have been synthesized via a general surfactant-assisted template method, involving the formation of porous metal oxides coated with 1-hexadecylamine (HDA) and a subsequent thermal treatment. The presence of HDA is of importance for the formation of a porous structure, and the successive pyrolysis of such a nitrogen-containing surfactant generates nitrogen-doped carbon (N-C) coated on the surface of metal oxides, which also provides a facile way to adjust the valence states of metal oxides via the carbothermal reduction reaction. When used as electrode materials, the highly porous metal oxides with N-C coating exhibited enhanced performance for lithium ion storage, thanks to the unique 3D structures associated with highly porous structure and thin N-C coating. Typically, the porous metal oxides (V2O5, MoO3, MnO2) exhibited discharge capacities of 286, 303, and 463 mAh g(-1) at current densities of 30 and 100 mA g(-1), respectively. In contrast, the metal oxides with low valences and carbon coating (VO2@N-C, MoO2@N-C, and MnO@N-C) exhibited improved capacities of 461, 613, and 892 mAh g(-1). The capacity retentions of about 87.5, 80.2, and 85.0% for VO2@N-C, MoO2@N-C, and MnO@N-C were achieved after 600 cycles, suggesting the acceptable cycling stability. The present strategy would provide general guidance for preparing porous metal oxide foams with enhanced lithium storage performances.
Keywords: lithium storage; metal oxide foam; nitrogen-doped carbon; porous structure; surfactant.