A comparative and in-depth investigation on the reactivity of various Li-based electrolytes and of the solid electrolyte interface (SEI) formed at graphite electrode is carried out using X-ray photoelectron spectroscopy (XPS), chemical simulation test, and differential scanning calorimetry (DSC). The electrolytes investigated include LiX (X = PF6, TFSI, TDI, FSI, and FTFSI), dissolved in EC-DMC. The reactivity and SEI nature of electrolytes containing the relatively new imide (LiFSI and LiFTFSI) and imidazole (LiTDI) salts are evaluated and compared to those of well-researched LiPF6(-) and LiTFSI-based electrolytes. The thermal reactivity of LixC6 in the various electrolytes is found to be in the order of LiFSI > LiTDI > LiTFSI > LiFTFSI > LiPF6 and LiFSI > LiFTFSI > LiPF6 > LiTFSI > LiTDI in terms of onset exothermic temperature and total heat generated, respectively. Surface and depth-profiling XPS analysis of the SEI formed with the diverse electrolyte formulations provide insight into the differences and similarities (composition, thickness, and evolution, etc.) emanating from the structure of the various salt anions.
Keywords: Li-ion battery; SEI layer; XPS; electrolyte; imidazole; imide; solid−electrolyte interphase.