Highly repeatable and recoverable phototransistors were explored using a "multifunctional channels" structure with multistacked chalcogenide and oxide semiconductors. These devices were made of (i) photoactive CdS (with a visible band gap), (ii) fast charge transporting ZnO (with a high field-effect mobility), and (iii) a protection layer of Al2O3 (with high chemical durability). The CdS TFT without the Al2O3 protection layer did not show a transfer curve due to the chemical damage that occurred on the ZnO layer during the chemical bath deposition (CBD) process used for CdS deposition. Alternatively, compared to CdS phototransistors with long recovery time and high hysteresis (ΔVth = 19.5 V), our "multi-functional channels" phototransistors showed an extremely low hysteresis loop (ΔVth = 0.5V) and superior photosensitivity with repeatable high photoresponsivity (52.9 A/W at 400 nm). These improvements are likely caused by the physical isolation of the sensing region and charge transport region by the insertion of the ultrathin Al2O3 layer. This approach successfully addresses some of the existing problems in CdS phototransistors, such as the high gate-interface trap site density and high absorption of molecular oxygen, which originate from the polycrystalline CdS.
Keywords: cadmium sulfide; charge transport layer; multifunctional channels; oxide semiconductor; phototransistor; visible light.