Nanofibrillated cellulose from tobacco industry wastes

Glaiton Tuzzin; Marcelo Godinho; Aline Dettmer; Ademir José Zattera

doi:10.1016/j.carbpol.2016.04.045

Nanofibrillated cellulose from tobacco industry wastes

Carbohydr Polym. 2016 Sep 5:148:69-77. doi: 10.1016/j.carbpol.2016.04.045. Epub 2016 Apr 12.

Authors

Glaiton Tuzzin¹, Marcelo Godinho¹, Aline Dettmer², Ademir José Zattera¹

Affiliations

¹ Engineering of Processes and Technologies Post-Graduate Program, University of Caxias do Sul, Caxias do Sul, Rio Grande do Sul, Brazil.
² Engineering of Processes and Technologies Post-Graduate Program, University of Caxias do Sul, Caxias do Sul, Rio Grande do Sul, Brazil. Electronic address: alinedettmer@gmail.com.

PMID: 27185117
DOI: 10.1016/j.carbpol.2016.04.045

Abstract

Tobacco stems waste underwent steam explosion pulping for nanofibrillated cellulose (NFC) production. In order to obtain NFC hydrogels, the pulp obtained by steam explosion was bleached and refined in a grinder employing specific energy of up to 5067kWh/t. Eucalyptus kraft pulp was processed under the same conditions to produce NFC hydrogels, later used in order to compare with NFC hydrogels from tobacco stems waste. According to statistical analysis, the optimum tobacco stems pulping condition was obtained with a severity index of log3.0 and active alkali of 16.25%. These conditions allowed obtaining a bleached pulp with Schopper Riegler degree of 46. Electronic microscopy with field emission showed a higher presence of nanofibers in the tobacco stems pulp than in commercial eucalyptus kraft pulp, both after refining. Thermal analysis indicated that tobacco stems pulp degrade at lower temperatures than eucalyptus kraft pulp. FTIR analysis did not indicate chemical bonding differences between the two pulps.

Keywords: Nanocellulose; Steam explosion; Tobacco; Waste.