Biodegradable calcium phosphate cements (CPCs) are promising materials for minimally invasive treatment of bone defects. However, CPCs have low mechanical strength and fracture toughness. One approach to overcome these limitations is the modification of the CPC with reinforcing fibers. The matrix-fiber interfacial shear strength (ISS) is pivotal for the biomechanical properties of fiber-reinforced CPCs. The aim of the current study was to control the ISS between a brushite-forming CPC and degradable PLGA fibers by oxygen plasma treatment and to analyze the impact of the ISS alterations on its bulk mechanical properties. The ISS between CPC matrix and PLGA fibers, tested in a single-fiber pull-out test, increased up to 2.3-fold to max. 3.22±0.92MPa after fiber oxygen plasma treatment (100-300W, 1-10min), likely due to altered surface chemistry and morphology of the fibers. This ISS increase led to more efficient crack bridging and a subsequent increase of the post-peak residual strength at biomechanically relevant, moderate strains (up to 1%). At the same time, the work of fracture significantly decreased, possibly due to an increased proportion of fractured fibers unable to further absorb energy by frictional sliding. Flexural strength and flexural modulus were not affected by the oxygen plasma treatment. This study shows for the first time that the matrix-fiber ISS and some of the resulting mechanical properties of fiber-reinforced CPCs can be improved by chemical modifications such as oxygen plasma treatment, generating the possibility of avoiding catastrophic failures at the implant site and thus enhancing the applicability of biodegradable CPCs for the treatment of (load-bearing) bone defects.
Keywords: Calcium phosphate cement; Fiber reinforcement; Interfacial shear strength; Mechanical properties; Plasma treatment.
Copyright © 2016 Elsevier Ltd. All rights reserved.