Oriented Nucleation of both Ge-Fresnoite and Benitoite/BaGe4O9 during the Surface Crystallisation of Glass Studied by Electron Backscatter Diffraction

Wolfgang Wisniewski; Marek Patschger; Steliana Murdzheva; Christian Thieme; Christian Rüssel

doi:10.1038/srep20125

Oriented Nucleation of both Ge-Fresnoite and Benitoite/BaGe4O9 during the Surface Crystallisation of Glass Studied by Electron Backscatter Diffraction

Sci Rep. 2016 Feb 8:6:20125. doi: 10.1038/srep20125.

Authors

Wolfgang Wisniewski¹, Marek Patschger¹, Steliana Murdzheva¹, Christian Thieme¹, Christian Rüssel¹

Affiliation

¹ Otto-Schott-Institut, Jena University, Fraunhoferstr. 6, 07743 Jena, Germany.

Abstract

Two glasses of the compositions 2 BaO - TiO2 - 2.75 GeO2 and 2 BaO - TiO2 -3.67 GeO2 (also known as BTG55) are annealed at temperatures from 680 to 970 °C to induce surface crystallization. The resulting samples are analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM) including electron backscatter diffraction (EBSD). Ge-Fresnoite (Ba2TiGe2O8, BTG) is observed at the immediate surface of all samples and oriented nucleation is proven in both compositions. After a very fast kinetic selection, the crystal growth of BTG into the bulk occurs via highly oriented dendrites where the c-axes are oriented perpendicular to the surface. The growth of this oriented layer is finally blocked by dendritc BTG originating from bulk nucleation. The secondary phases BaTiGe3O9 (benitoite) and BaGe4O9 are also identified near the surface by XRD and localized by EBSD which additionally indicates orientation preferences for these phases. This behaviour is in contrast with previous reports from the Ba2TiSi2O8 as well as the Sr2TiSi2O8 systems.

Publication types