The surface-grafted poly(hydroxylethyl methacrylate) (PHEMA) molecules were demonstrated to show a brush state regardless of their molecular length (molecular weight). Adsorption of proteins from 10% fetal bovine serum (FBS), fibronectin (Fn) and bovine serum albumin (BSA) was quantified by ellipsometry, revealing that the amounts of FBS and Fn decreased monotonously along with the increase of PHEMA thickness, whereas not detectable for BSA when the PHEMA thickness was larger than 6 nm. Radio immunoassay found that the adsorption of Fn from 10% FBS had no significant difference regardless of the PHEMA thickness. However, ELISA results showed that the Arg-Gly-Asp (RGD) activity of adsorbed Fn decreased with the increase of PHEMA thickness. By comparison of cellular behaviors of vascular smooth muscle cells (VSMCs) being cultured in vitro in the normal serum-containing medium and the Fn-depleted serum-containing medium, the significant role of Fn on modulating the adhesion and migration of VSMCs was verified. Taking account all the results, the Fn adsorption model and its role on linking the biomaterials surface to the VSMCs behaviors are proposed.
Keywords: migration; poly(hydroxylethyl methacrylate); protein adsorption; smooth muscle cells.