Effect of boron oxide addition on the viscosity-temperature behaviour and structure of phosphate-based glasses

J Biomed Mater Res B Appl Biomater. 2017 May;105(4):764-777. doi: 10.1002/jbm.b.33610. Epub 2016 Jan 9.

Abstract

In this study, nine phosphate-based glass formulations from the system P2 O5 -CaO-Na2 O-MgO-B2 O3 were prepared with P2 O5 content fixed as 40, 45 and 50 mol%, where Na2 O was replaced by 5 and 10 mol% B2 O3 and MgO and CaO were fixed to 24 and 16 mol%, respectively. The effect of B2 O3 addition on the viscosity-temperature behaviour, fragility index and structure of the glasses was investigated. The composition of the glasses was confirmed by ICP-AES. The viscosity-temperature behaviour of the glasses were measured using beam-bending and parallel -plate viscometers. The viscosity of the glasses investigated was found to shift to higher temperature with increasing B2 O3 content. The kinetic fragility parameter, m and F1/2 , estimated from the viscosity curve were found to decease with increasing B2 O3 content. The structural analysis was achieved by a combination of Fourier transform infrared spectroscopy and solid state nuclear magnetic resonance. 31 P solid-state magic-angle-spinning nuclear magnetic resonance (MAS-NMR) showed that the local structure of the glasses changes with increasing B2 O3 content. As B2 O3 was added to the glass systems, the phosphate connectivity increases as the as the Q1 units transforms into Q2 units. The 11 B NMR results confirmed the presence of tetrahedral boron (BO4 ) units for all the compositions investigated. Structural analysis indicates an increasing level of cross-linking with increasing B2 O3 content. Evidence of the presence of P-O-B bonds was also observed from the FTIR and 31 P NMR analysis. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 764-777, 2017.

Keywords: FTIR; MAS-NMR; fragility; phosphate-based glass; viscosity.

MeSH terms

  • Boron Compounds / chemistry*
  • Ceramics / chemical synthesis*
  • Ceramics / chemistry*
  • Hot Temperature*
  • Phosphates / chemistry*
  • Viscosity

Substances

  • Bioglass
  • Boron Compounds
  • Phosphates
  • boron oxide