Novel two-step method to form silk fibroin fibrous hydrogel

Abstract

Hydrogels prepared by silk fibroin solution have been studied. However, mimicking the nanofibrous structures of extracellular matrix for fabricating biomaterials remains a challenge. Here, a novel two-step method was applied to prepare fibrous hydrogels using regenerated silk fibroin solution containing nanofibrils in a range of tens to hundreds of nanometers. When the gelation process of silk solution occurred, it showed a top-down type gel within 30min. After gelation, silk fibroin fibrous hydrogels exhibited nanofiber network morphology with β-sheet structure. Moreover, the compressive stress and modulus of fibrous hydrogels were 31.9±2.6 and 2.8±0.8kPa, respectively, which was formed using 2.0wt.% concentration solutions. In addition, fibrous hydrogels supported BMSCs attachment and proliferation over 12days. This study provides important insight in the in vitro processing of silk fibroin into useful new materials.

Keywords: Fibrous; Hydrogel; Silk fibroin.