Background: To compare the shear bond strength of brackets with and without enamel etching.
Material and methods: In this study, 60 sound premolars were randomly divided into four different groups: 1- TXE group: Enamel etching+Transbond XT adhesive+ Transbond XT composite. 2- TXS group: Transbond plus self-etch adhesive+ Transbond XT composite. 3- PQ1E group: Enamel etching+ PQ1 adhesive+ Transbond XT composite. 4- PQ1 group: PQ1 adhesive+ Transbond XT composite. The shear bond strengths of brackets were evaluated using universal testing machine at cross head speed of 0.5 mm/min. The Adhesive Remnant Index (ARI) was also measured. One-way ANOVA, Tukey's post hoc, Kruskal-wallis and Mann-Witney U test were used for data analysis.
Results: There was a significant difference between etched and unetched groups respect to SBS and ARI (p<0.05), however; no significant difference was observed between unetched group and self-etch adhesive group (p>> 0.05). The shear bond strength of PQ1 group was the least but in acceptable range and its ARI was less than other groups.
Conclusions: PQ1 adhesive can be used for bracket bonding without enamel etching with adequate bond strength and minimal ARI.
Key words: Bracket, shear bond strength, filled-adhesive, self-etch adhesive.