CeO2-CuO nanorods with mesoporous structure were synthesized by a facile and mild strategy, which involves an interfacial reaction between Ce2(SO4)3 precursor and NaOH ethanol solution at room temperature to obtain mesoporous CeO2 nanorods, followed by a solvothermal treatment of as-prepared CeO2 and Cu(CH3COO)2. Upon solvothermal treatment, CuO species is highly dispersed onto the CeO2 nanorod surface to form CeO2-CuO composites, which still maintain the mesoporous feature. A preliminary CO catalytic oxidation study demonstrated that the CeO2-CuO samples exhibited strikingly high catalytic activity, and a high CO conversion rate was observed without obvious loss in activity even after thermal treatment at a high temperature of 500 °C. Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and hydrogen temperature-programmed reduction (H2-TPR) analysis revealed that there is a strong interaction between CeO2 and CuO. Moreover, it was found that the introduction of CuO species into CeO2 generates oxygen vacancies, which is highly likely to be responsible for high catalytic activity toward CO oxidation of the mesoporous CeO2-CuO nanorods.
Keywords: bimetal oxide; catalysis; ceria; composites; interfacial reaction.