Preheating of dental composites improves their flowability, facilitating successful restorations. However, the flowability of dental composites is affected not only by temperature but also by the deformation conditions. In the present work, the effects of various deformation conditions upon the viscoelastic properties of a preheated dental composite were studied. The rheological properties of Z350 dental composites at 25, 45, and 60°C were measured by a strain-controlled rheometer. When a low strain (0.03%) was applied, the preheated composite exhibited greater shear storage modulus (G') and complex viscosity (η*) than a room-temperature composite. Oppositely, when a high strain (50%) was applied, G' and η* of a preheated composite were lower than those of a room-temperature composite. Preheating of dental composites might be helpful in clinical practice both to increase the slumping resistance when minimal manipulation is used (e.g., during the build-up of a missing cusp tip) and to increase flowability when manipulation entailing high shear strain is applied (e.g., when uncured composite resin is spread on a dentin surface).