With increasing interest in GaN based devices, the control and evaluation of doping are becoming more and more important. We have studied the structural and electrical properties of a series of Si-doped GaN nanowires (NWs) grown by molecular beam epitaxy (MBE) with a typical dimension of 2-3 μm in length and 20-200 nm in radius. In particular, high resolution energy dispersive X-ray spectroscopy (EDX) has illustrated a higher Si incorporation in NWs than that in two-dimensional (2D) layers and Si segregation at the edge of the NW with the highest doping. Moreover, direct transport measurements on single NWs have shown a controlled doping with resistivity from 10(2) to 10(-3) Ω·cm, and a carrier concentration from 10(17) to 10(20) cm(-3). Field effect transistor (FET) measurements combined with finite element simulation by NextNano(3) software have put in evidence the high mobility of carriers in the nonintentionally doped (NID) NWs.
Keywords: EDX; GaN; Si doping; electron mobility; field effect transistor; four probe resistivity; nanowires.