Enhanced Performance of "Flower-like" Li4Ti5O12 Motifs as Anode Materials for High-Rate Lithium-Ion Batteries

Abstract

"Flower-like" motifs of Li4Ti5O12 were synthesized by using a facile and large-scale hydrothermal process involving unique Ti foil precursors followed by a short, relatively low-temperature calcination in air. Moreover, a detailed time-dependent growth mechanism and a reasonable reaction scheme were proposed to clearly illustrate and highlight the structural evolution and subsequent formation of this material. Specifically, the resulting "flower-like" Li4Ti5O12 microspheres consisting of thin nanosheets provide for an enhanced surface area and a reduced lithium-ion diffusion distance. The high surface areas of the exposed roughened, thin petal-like component nanosheets are beneficial for the interaction of the electrolyte with Li4Ti5O12 , which thereby ultimately provides for improved high-rate performance and favorable charge/discharge dynamics. Electrochemical studies of the as-prepared nanostructured Li4Ti5O12 clearly revealed their promising potential as an enhanced anode material for lithium-ion batteries, as they present both excellent rate capabilities (delivering 148, 141, 137, 123, and 60 mAh g(-1) under discharge rates of 0.2, 10, 20, 50, and 100 C, at cycles of 50, 55, 60, 65, and 70, respectively) and stable cycling performance (exhibiting a capacity retention of ≈97 % from cycles 10-100, under a discharge rate of 0.2 C, and an impressive capacity retention of ≈87 % by using a more rigorous discharge rate of 20 C from cycles 101-300).

Keywords: batteries; energy conversion; flower-like structures; hydrothermal synthesis; lithium.