Synthesis, growth and characterization of a new promising organic nonlinear optical crystal: 4-Nitrophenyl hydrazone

B C Hemaraju; M A Ahlam; N Pushpa; K M Mahadevan; A P Gnana Prakash

doi:10.1016/j.saa.2015.07.031

Synthesis, growth and characterization of a new promising organic nonlinear optical crystal: 4-Nitrophenyl hydrazone

Spectrochim Acta A Mol Biomol Spectrosc. 2015 Dec 5:151:854-60. doi: 10.1016/j.saa.2015.07.031. Epub 2015 Jul 7.

Authors

B C Hemaraju¹, M A Ahlam¹, N Pushpa², K M Mahadevan³, A P Gnana Prakash⁴

Affiliations

¹ Department of Studies in Physics, University of Mysore, Mysore 570 006, India.
² Department of PG Studies in Physics, JSS College, Ooty Road, Mysore 570025, India.
³ Department of PG Studies in Pharmaceutical Chemistry, Kuvempu University Kadur P.G. Center, Kadur 577 548, Karnataka, India.
⁴ Department of Studies in Physics, University of Mysore, Mysore 570 006, India. Electronic address: gnanaprakash@physics.uni-mysore.ac.in.

PMID: 26184469
DOI: 10.1016/j.saa.2015.07.031

Abstract

4-Nitrophenyl hydrazone single crystals were grown by slow evaporation of solvent method using acetone as a solvent. The grown crystals were subjected to various characterizations such as X-ray diffraction studies, UV-visible studies, thermogravimetric analysis and differential thermal analysis (TGA/DTA) and second harmonic generation (SHG). The cell parameters were calculated by using single crystal XRD measurement and the crystal system was found as orthorhombic with non-centro-symmetric space group Pca21. The crystallinity of the grown crystal was confirmed by powder X-ray diffraction analysis. The Fourier transform infrared (FTIR) and nuclear magnetic resonance (NMR) studies confirmed the presence of functional groups in the sample. The optical transmittance spectrum shows that the crystal is transparent in the visible wavelength range. The scanning electron microscopy (SEM) was used to study the surface morphology of the grown crystal. The chemical composition of the grown crystal was confirmed by energy dispersive X-ray (EDX) analysis. The TGA/DTA results showed that the material is stable up to 146°C. The NLO property of the crystal was confirmed by Kurtz and Perry method and SHG conversion efficiency is 15.39 times when compared to KDP crystal.

Keywords: Crystal structure; Nonlinear optical materials; Optical properties; SHG; X-ray diffraction.