Fine-tuning of particle size and morphology has been shown to result in differential material performance in the area of secondary lithium-ion batteries. For instance, reduction of particle size to the nanoregime typically leads to better transport of electrochemically active species by increasing the amount of reaction sites as a result of higher electrode surface area. The spinel-phase oxide LiNi0.5Mn1.5O4 (LNMO), was prepared using a sol-gel based template synthesis to yield nanowire morphology without any additional binders or electronic conducting agents. Therefore, proper experimentation of the nanosize effect can be achieved in this study. The spinel phase LMNO is a high energy electrode material currently being explored for use in lithium-ion batteries, with a specific capacity of 146 mAh/g and high-voltage plateau at ∼4.7 V (vs Li/Li(+)). However, research has shown that extensive electrolyte decomposition and the formation of a surface passivation layer results when LMNO is implemented as a cathode in electrochemical cells. As a result of the high surface area associated with nanosized particles, manganese ion dissolution results in capacity fading over prolonged cycling. In order to prevent these detrimental effects without compromising electrochemical performance, various coating methods have been explored. In this work, TiO2 and Al2O3 thin films were deposited using atomic layer deposition (ALD) on the surface of LNMO particles. This resulted in effective surface protection by prevention of electrolyte side reactions and a sharp reduction in resistance at the electrode/electrolyte interface region.
Keywords: ALD; LiNi0.5Mn1.5O4 spinel; cation dissolution; nano-structured electrode; surface modification.