Hybrid supercapacitors (battery-supercapacitor hybrid devices, HSCs) deliver high energy within seconds (excellent rate capability) with stable cyclability. One of the key limitations in developing high-performance HSCs is imbalance in power capability between the sluggish Faradaic lithium-intercalation anode and rapid non-Faradaic capacitive cathode. To solve this problem, we synthesize Nb2O5@carbon core-shell nanocyrstals (Nb2O5@C NCs) as high-power anode materials with controlled crystalline phases (orthorhombic (T) and pseudohexagonal (TT)) via a facile one-pot synthesis method based on a water-in-oil microemulsion system. The synthesis of ideal T-Nb2O5 for fast Li(+) diffusion is simply achieved by controlling the microemulsion parameter (e.g., pH control). The T-Nb2O5@C NCs shows a reversible specific capacity of ∼180 mA h g(-1) at 0.05 A g(-1) (1.1-3.0 V vs Li/Li(+)) with rapid rate capability compared to that of TT-Nb2O5@C and carbon shell-free Nb2O5 NCs, mainly due to synergistic effects of (i) the structural merit of T-Nb2O5 and (ii) the conductive carbon shell for high electron mobility. The highest energy (∼63 W h kg(-1)) and power (16 528 W kg(-1) achieved at ∼5 W h kg(-1)) densities within the voltage range of 1.0-3.5 V of the HSC using T-Nb2O5@C anode and MSP-20 cathode are remarkable.
Keywords: controlled crystal structures; core−shell nanostructures; high-power anodes; hybrid supercapacitors; orthorhombic Nb2O5 nanocrystals.