Aim: To evaluate the effect of fiber post surface treatments on push-out bond strength between fiber post and root dentin.
Materials and methods: Sixty bovine mandibular teeth (N=60) were sectioned (16 mm), prepared (12 mm), embedded with acrylic resin and then allocated into six groups (n=10): Gr1- Silane coupling agent (Sil)+Conventional resin cement AllC em (Al C); Gr2- Sil+Conventional resin cement RelyX ARC (ARC); Gr3- tribochemical silica coating (TBS)+AlC; Gr4- TBS+ARC; Gr5- No treatment (NT)+AlC; Gr6- NT+ ARC. Specimens were sectioned in four slices (2 mm) and submitted to push-out test. Fracture analyses were executed at x200. The values of the push-out bond strength were submitted to two-way ANOVA and Tukey test (α=0.05).
Results: Resincement did not affect the bond strength values (p=0.9674), fiber post surface treatment affected the push-out bond strength (p=0.0353), interaction between factors did not affected the values (p=0.338). Tukey test did not show differences between the groups. Adhesive failure between cement and dentin was predominantly.
Conclusion: The fiber post surface treatment appears have no Influence on bond strength between fiber post and root dentin.
Clinical significance: The tested fiber posts surface treatment appears do not Influence the fiber post bond behavior.
Keywords: Adhesion; Fiber post surface conditioning; Intraradicular dentin; Push-out test.