Controllable bandgap widening from 1.8 to 2.6 eV is reported from oxidized MoS2 sheets that are composed of quilted phases of various MoSxOy flakes. The exfoliated flakes have large size (≥100 μm × 100 μm) sheets with average thickness of 1.7 nm. Remarkably, fine reversible tuning of the bandgap is achieved by postprocessing sulfurization of the MoSxOy sheets.
Keywords: 2D transition metal dichalcogenides; bandgap widening; intercalation compounds; molybdenum disulfide; photoluminescence.
© 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.