Effect of ion release from Cu-doped 45S5 Bioglass® on 3D endothelial cell morphogenesis

Abstract

Both silicate-based bioactive glasses and copper ions have demonstrated angiogenic activity and therefore represent promising bioinorganic agents for the promotion of vascularization in tissue-engineered scaffolds. This study examined the effect of ionic release products from 45S5 Bioglass® doped with 0 and 2.5 wt.% CuO (BG and Cu-BG respectively) on the formation of capillary-like networks by SVEC4-10 endothelial cells (ECs) seeded in a three-dimensional (3D) type I collagen matrix. Copper and silicon release following 24h dissolution increased non-proportionally with Cu-BG concentration in cell culture medium, while calcium levels were decreased below the initial medium concentration. EC network length, connectivity, branching, quantified by means of a 3D morphometric image analysis method, as well as proliferation and metabolic activity were reduced in a dose-dependent fashion by BG and Cu-BG ionic release products. This reduction was less prominent for BG compared to an equivalent concentration of Cu-BG, which was attributed to a lower extent of silicon release and calcium consumption. Moreover, a CuCl2 dose equivalent to the highest concentration of Cu-BG exhibited no effect on ECs. In conclusion, while the previously reported pro-angiogenic activity of both Bioglass® and copper may not be reflected in a direct response of ECs, this study provides a maximum glass concentration for non-harmful angiogenic stimulation to be examined in future work.

Keywords: Angiogenesis; Bioactive glass; Bioinorganics; Capillary-like network; Copper.